Method of fabricating a semiconductor device

ABSTRACT

A method of fabricating a semiconductor device is provided. The method of fabricating the semiconductor device comprises providing a substrate. Next, an insulating layer, a conductive layer and a silicide layer are formed on the substrate in sequence. Next, a hard masking layer is formed on the silicide layer exposing a portion of the silicide layer. A first etching step is performed to remove the silicide layer and the underlying conductive layer which are not covered by the hard masking layer, thereby forming a gate stack. And next, a second etching step is performed to remove any remaining conductive layer not covered by the hard masking layer after the first etching step. The second etching step is performed with an etchant comprising ammonium hydroxide.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates to a method of fabricating a semiconductor device, and more particularly, relates to a method of fabricating a gate stack of a semiconductor device.

2. Description of the Related Art

In recent years, semiconductor device fabricating technology has continually sought new ways to achieve high device performance, low cost, and great device densities. For example, in the case of a dynamic random access memory (DRAM), high device densities can be used for forming trench capacitor structures during DRAM fabrication. Additionally, while reducing device critical dimension (CD), word line (WL) or so-called gate conductor (GC) stacks of DRAM cells will also be shrunk.

Nevertheless, for conventional WL etching processes, precision is limited due to the uneven topography of the laminate layers for subsequent WL etching given the differentiated step height of the underlying shallow trench isolations (STI). Specifically, WL etched on uneven topography results in bridge problems with WL to WL shorting due to under-etching and device leakage and failure problems with WL punch through due to over-etching. As a result, the conventional WL etching processes increases device defect density and unreliability.

Thus, a novel and reliable method of fabricating a gate stack of a semiconductor device for reducing WL to WL short and device leakage is needed.

BRIEF SUMMARY OF INVENTION

To solve the above-described problems, a method of fabricating a semiconductor device is provided. An exemplary embodiment of a method of fabricating a semiconductor device comprises providing a substrate. Next, an insulating layer, a conductive layer and a silicide layer are sequentially formed on top of the substrate. A patterned hard masking layer is next formed on the silicide layer exposing a portion of the silicide layer. A first etching step is performed to partially remove the silicide layer and the underlying conductive layer which are not covered by the hard masking layer, thereby forming a gate stack. And next, a second etching step is performed to remove residue of any remaining conductive layer not covered by the hard masking layer after the first etching step. The second etching step is performed with an etchant comprising ammonium hydroxide.

Another exemplary embodiment of a method of fabricating a semiconductor device comprises providing a substrate. Next, an insulating layer, a conductive layer and a silicide layer are sequentially formed on the substrate in sequence. Next, a patterned hard masking layer is formed on the silicide layer exposing a portion of the silicide layer. A first etching step is performed to partially remove the silicide layer and the underlying conductive layer which are not covered by the hard masking layer, thereby forming a gate stack. Next, a second etching step is performed to remove residue of the any remaining conductive layer not covered by the hard masking layer after the first etching step. The second etching step is performed with an etchant comprising ammonium hydroxide. And next, a third etching step is performed to remove a portion of the silicide layer of the gate stack so as to allow the silicide layer to have a neck after the second etching step.

A detailed description is given in the following embodiments with reference to the accompanying drawings.

BRIEF DESCRIPTION OF DRAWINGS

The invention can be more fully understood by reading the subsequent detailed description and examples with references made to the accompanying drawings, wherein:

FIGS. 1 to 6 show cross sections of an exemplary embodiment of a process of fabricating a semiconductor device.

DETAILED DESCRIPTION OF INVENTION

The following description is of the best-contemplated mode of carrying out the invention. This description is made for the purpose of illustrating the general principles of the invention and should not be taken in a limiting sense. The scope of the invention is best determined by reference to the appended claims.

FIGS. 1 to 6 show cross sections of an exemplary embodiment of a process of fabricating a semiconductor device. Wherever possible, the same reference numbers are used in the drawings and the descriptions to refer to the same or like parts.

FIGS. 1 to 6 are cross sections showing an exemplary embodiment of a method for fabricating a gate stack. Referring to FIG. 1, a substrate 200 is provided. The substrate 200 is preferably a silicon substrate. Also, the substrate 200 may comprise SiGe silicon on insulator (SOI), and other commonly used semiconductor substrates can be used. In one embodiment, a plurality of shallow trench isolations (STI) (not shown) is formed in the substrate 200 to isolate subsequent semiconductor devices. The shallow trench isolations (STI) may be formed by etching the substrate 200 to form recesses. Next, a dielectric material such as a high-density plasma oxide (HDP oxide) is filled in the recesses. A planarization process such as chemical mechanical polish (CMP) is performed to remove the excessive dielectric material on top of the substrate 200 to form STIs in the substrate 200. An insulating layer 202 is then formed on the substrate 200 by methods such as thermal oxidation, chemical vapor deposition (CVD), or atomic layer CVD (ALCVD). The insulating layer 202 may comprise oxide, nitride, oxynitride, oxycarbide or combinations thereof. The insulating layer 202 may also comprise high-dielectric constant (k) (k>8) dielectric materials such as aluminum oxide (Al₂O₃), hafnium oxide (HfO₂), hafnium oxynitride (HfON), hafnium silicate (HfSiO4), zirconium oxide (ZrO₂); zirconium oxynitride (ZrON, zirconium silicate (ZrSiO₄), yttrium oxide (Y₂O₃), lanthalum oxide (La₂O₃), cerium oxide (CeO₂), titanium oxide (TiO₂), tantalum oxide (Ta₂O₅) or combinations thereof. In one embodiment, the insulating layer 202 is used as a gate insulating layer of the semiconductor device.

Referring to FIG. 2, a conductive layer 204 is next formed on the insulating layer 202 by thin film deposition processes such as CVD. The conductive layer 204 may comprise silicon or polysilicon. The conductive layer 204 is preferably doped to reduce sheet resistance. Alternatively, the conductive layer 204 may comprise amorphous silicon. Next, a silicide layer 206 is formed on the conductive layer 204 by methods such as thermal CVD with tungsten source material comprising WF₆ and silicon source material comprising SiH₄. In one embodiment, the silicide layer 206 may be a polycide layer formed of WSi. The silicide layer 206 can efficiently reduce contact resistance of the conductive layer 204. Next, a hard masking layer 208 is formed on the silicide layer 206. The hard masking layer 208 may comprise a nitride layer such as silicon nitride (Si₃N₄) formed by CVD. In one embodiment, the conductive layer 204 serves as a gate of the semiconductor device.

Referring to FIG. 3, a photoresist layer may cover the entire region (not shown). Next, a portion of the hard masking layer 208 is removed by photolithography and etching to form a patterned hard masking layer 208 a. The photoresist layer is then removed.

Referring to FIG. 4, a first etching step is performed to remove the silicide layer 206 and the underlying conductive layer 204 which are not covered by the patterned hard masking layer 208 a, by dry etching with an etchant such as Cl₂, HCl, SF₆, O₂ or combinations thereof, thereby forming a gate stack 210. The gate stack 210 comprises a silicide layer 206 a and a conductive layer 204 a.

FIG. 5 illustrates a method of removing any remaining conductive layer 204 b. A second etching step is performed to remove any remaining conductive layer 204 b not covered by the patterned hard masking layer 208 a after the first etching step, with an etchant comprising ammonium hydroxide (NH₄OH). In one embodiment, the second etching step is used to remove any remaining conductive layer 204 b having a thickness between 5 Å to 100 Å at a temperature of around 25° C. to 30° C., preferably 25° C. The second etching step may comprise wet etching with an etchant comprising ammonium hydroxide (NH₄OH) dissolving in hydrogen oxide (H₂O). A volume ratio of NH₄OH and H₂O can be properly adjusted to achieve any profile required for the conductive layer 204 a while removing the remaining conductive layer 204 b. For example, the etchant comprising NH₄OH and H₂O preferably has a volume ratio of around 1:100 to 1:200, such that a conductive layer 204 a critical dimension loss is controlled at less than 7%. Ammonium hydroxide (NH₄OH) of the etchant preferably comprises industrial NH₄OH with a weight concentration of around 35 wt % to 45 wt %, preferably 40 wt %. The insulating layer 202 such as oxide is not damaged during the second etching step due to higher etching selectivity to oxide of NH₄OH.

FIG. 6 illustrates a formation of a gate stack 210 a. A third etching step is performed by removing a portion of the silicide layer 206 a of the gate stack 210 to form a silicide layer 206 b and a gate stack 210 a. The third etching step may be a wet etching step using standard clean 1 (SC-1). SC-1 also referred to as ammonium hydrogen peroxide mixture (APM), comprises a solvent of ammonium hydroxide (NH₄OH)/hydrogen peroxide (H₂O₂)/hydrogen oxide (H₂O) with a volume ratio of about 1:1:5. After performing the third etching step, a sidewall of the silicide layer 206 b is recessed to form a neck between the patterned hard masking layer 208 a and the conductive layer 204 a. Thus, completing the formation of a semiconductor device 250.

In the exemplary embodiment of the semiconductor device 250, the second etching step is performed with an etchant comprising ammonium hydroxide (NH₄OH) to remove any remaining conductive layer 204 b not covered by the hard masking layer 208 a after forming the gate stack 210 a by the first etching step. The second etching step can be performed under required volume ratio of the etchant or required temperature to achieve a required profile of the conductive layer 204 a while removing the remaining conductive layer 204 b. In addition, the second etching step eliminates semiconductor device problems such as shorting, device leakage and failure, or more specifically, bridge problems due to gate under-etching or gate punch through due to gate over-etching. Thus, decreasing device defect density and increasing device performance and reliability.

While the invention has been described by way of example and in terms of the preferred embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements. 

1. A method of fabricating a semiconductor device, comprising: providing a substrate; sequentially forming an insulating layer, a conductive layer and a silicide layer on top of the substrate; forming a patterned hard masking layer on the silicide layer to expose a portion of the silicide layer; performing a first etching to partially remove the silicide layer as well as the conductive layer underlying the removed silicide layer, thereby forming a gate stack; and performing a second etching step to remove residue of any remaining conductive layer, with an etchant comprising ammonium hydroxide (NH₄OH).
 2. The method of fabricating the semiconductor device as claimed in claim 1, further comprising: performing a third etching step to remove a portion of the silicide layer of the gate stack so as to allow the silicide layer to have a neck after the second etching step.
 3. The method of fabricating the semiconductor device as claimed in claim 2, wherein the third etching step is performed by a solvent of ammonium hydroxide (NH₄OH)/hydrogen peroxide (H₂O₂)/hydrogen oxide (H₂O) with a volume ratio of about 1:1:5.
 4. The method of fabricating the semiconductor device as claimed in claim 1, wherein the second etching step is performed to remove the conductive layer having a thickness of between 5 Å to 100 Å.
 5. The method of fabricating the semiconductor device as claimed in claim 1, wherein the second etching step is performed at a temperature of between 20° C. to 30° C.
 6. The method of fabricating the semiconductor device as claimed in claim 1, wherein the etchant comprise ammonium hydroxide (NH₄OH) dissolved in hydrogen oxide (H₂O) with a volume ratio of between 1:100 to 1:200.
 7. The method of fabricating, the semiconductor device as claimed in claim 3, wherein the etchant comprise ammonium hydroxide (NH₄OH) dissolved in hydrogen oxide (H₂O) with a volume ratio of between 1:100 to 1:200.
 8. The method of fabricating the semiconductor device as claimed in claim 3, wherein the etchant comprise ammonium hydroxide (NH₄OH) dissolved in hydrogen oxide (H₂O) with a volume ratio of between 1:100 to 1:200.
 9. The method of fabricating the semiconductor device as claimed in claim 1, wherein the insulating layer comprises oxide.
 10. The method of fabricating the semiconductor device as claimed in claim 1, wherein the conductive layer comprises silicon, polysilicon or amorphous silicon.
 11. The method of fabricating the semiconductor device as claimed in claim 1, wherein the silicide layer comprises tungsten silicide (WSi).
 12. The method of fabricating the semiconductor device as claimed in claim 1, wherein the patterned hard masking layer comprises nitride. 